Abstract

We have investigated the magnetocaloric properties of Ln_0.67Ba_0.33Mn_{1 − x}Fe_xO₃ (Ln = La or Pr) manganites with x = 0 and 0.05. All compounds present a maximum and large magnetocaloric effect near the Curie temperature (T_C). The associated maximum value of the magnetic entropy change, at 5 T applied change in the magnetic field, is 4.37 J.kg^{− 1}.K^{− 1} for Pr_0.67Ba_0.33MnO₃ manganite with a T_C value of 205 K. The corresponding relative cooling power (RCP) reaches 230 J.kg^{− 1}. All the samples present similar RCP values that are relatively high and are promising materials to be used in ecologically friendly magnetic refrigeration technology. Iron doping reduces both T_C and ΔS_M^max and spreads the temperature working range with an almost constant RCP and can then be used to tune the working conditions of a refrigerator device.