Mechanical and thermal properties of AlN–BN–SiC ceramicsstar, open




Andrew A. Buchheita, E-mail The Corresponding Author, Greg E. Hilmasa, Corresponding Author Contact Information, E-mail The Corresponding Author, William G. Fahrenholtza, Douglas M. Deasonb and Hsin Wangc





aMaterials Science and Engineering Department, Missouri University of Science and Technology, Rolla, MO 65409, United States bU.S. Army Space & Missile Defense Command, Building 5220, Redstone Arsenal, AL 35898, United States cOak Ridge National Laboratory, High Temperature Materials Laboratory, Oak Ridge, TN 37831, USA




Received 5 July 2007; 


revised 8 April 2008; 


accepted 22 May 2008. 


Available online 13 June 2008.








Abstract


Mechanical and thermal properties were characterized for two AlN:BN:SiC composite ceramics produced from BN with different particle sizes. The ceramics were hot pressed at temperatures from 1950 to 2100 °C to not, vert, similar97% relative density. For both materials, the matrix (90:10 vol% SiC:AlN) had a grain size of not, vert, similar0.4 μm, and the BN grains (10 vol%) were crystallographically aligned. Microhardness values were between 20 and 22 GPa, while fracture toughness values were between 2.5 and 3.1 MPa m1/2. Other properties were found to be dependent on testing direction. Elastic moduli were between 260 and 300 GPa and strengths were not, vert, similar630 MPa for small particle BN additions. Thermal conductivity was calculated to be between 25 and 37 W/m K at room temperature and 17 and 25 W/m K at 900 °C. The low values compared to traditional SiC ceramics were attributed to AlN–SiC solid solution formation and sub-micron matrix grain sizes.





Keywords: Aluminum nitride; Boron nitride; Silicon carbide; Mechanical properties; Thermal properties; Hot pressing





Article Outline



1. Introduction
2. Experimental procedure

2.1. Powder processing
2.2. Densification
2.3. XRD
2.4. Microstructure
2.5. Mechanical properties
2.6. Thermal properties

3. Results and discussion

3.1. XRD
3.2. Density and microstructure
3.3. Mechanical properties
3.4. Thermal properties

4. Summary
Acknowledgements
References




Дизайн и программирование N-Studio 
А Б В Г Д Е Ё Ж З И Й К Л М Н О П Р С Т У Ф Х Ц Ч Ш Щ Ъ Ы Ь Э Ю Я
  • Chen Wev .  honorary member of ISSC science council

  • Harton Vladislav Vadim  honorary member of ISSC science council

  • Lichtenstain Alexandr Iosif  honorary member of ISSC science council

  • Novikov Dimirtii Leonid  honorary member of ISSC science council

  • Yakushev Mikhail Vasilii  honorary member of ISSC science council

  • © 2004-2019 ИХТТ УрО РАН
    беременность, мода, красота, здоровье, диеты, женский журнал, здоровье детей, здоровье ребенка, красота и здоровье, жизнь и здоровье, секреты красоты, воспитание ребенка рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок медицина, клиники и больницы, болезни, врач, лечение, доктор, наркология, спид, вич, алкоголизм православные знакомства, православный сайт творчeства, православные рассказы, плохие мысли, православные психологи рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок