The energetics of lanthanum tantalate materials





Tori Z. Forbesa, E-mail The Corresponding Author, May Nymanb, E-mail The Corresponding Author, Mark A. Rodriguezb, E-mail The Corresponding Author and Alexandra Navrotskya, Corresponding Author Contact Information, E-mail The Corresponding Author






a Peter A. Rock Thermochemistry Laboratory and NEAT ORU, University of California at Davis, Davis, CA 95616, USA


b Sandia National Laboratory, POB 5800, Albuquerque, NM 87185, USA





Received 6 May 2010; 


revised 11 August 2010; 


accepted 18 August 2010. 


Available online 22 August 2010.









Abstract



Lanthanum tantalates are important refractory materials with application in photocatalysis, solid oxide fuel cells, and phosphors. Soft-chemical synthesis utilizing the Lindqvist ion, [Ta6O19]8−, has yielded a new phase, La2Ta2O7(OH)2. Using the hydrated phase as a starting material, a new lanthanum orthotantalate polymorph was formed by heating to 850 °C, which converts to a previously reported LaTaO4 polymorph at 1200 °C. The stabilities of La2Ta2O7(OH)2 (LaTa−OH), the intermediate LaTaO4 polymorph (LaTa-850), and the high temperature phase (LaTa-1200) were investigated using high-temperature oxide melt solution calorimetry. The enthalpy of formation from the oxides were calculated from the enthalpies of drop solution to be −87.1±9.6, −94.9±8.8, and −93.1±8.7 kJ/mol for LaTa−OH, LaTa-850, and LaTa-1200, respectively. These results indicate that the intermediate phase, LaTa-850, is the most stable. This pattern of energetics may be related to cation–cation repulsion of the tantalate cations. We also investigated possible LnTaO4 and Ln2Ta2O7(OH)2 analogues of Ln=Pr, Nd to examine the relationship between cation size and the resulting phases.









Graphical abstract



The energetics of three lanthanum tantalates were investigated by the high-temperature oxide melt solution calorimetry. The enthalpies of formation from the oxides were calculated from the enthalpies of drop solution to be −87.1±9.6, −94.9±8.8, and −93.1±8.7 kJ/mol for La2Ta2O7(OH)2, LaTaO4 (850 °C), and LaTaO4 (1200 °C), respectively. These results indicate that the intermediate phase, LaTaO4 (850 °C), is the most stable in energy.






Дизайн и программирование N-Studio 
А Б В Г Д Е Ё Ж З И Й К Л М Н О П Р С Т У Ф Х Ц Ч Ш Щ Ъ Ы Ь Э Ю Я
  • Chen Wev .  honorary member of ISSC science council

  • Harton Vladislav Vadim  honorary member of ISSC science council

  • Lichtenstain Alexandr Iosif  honorary member of ISSC science council

  • Novikov Dimirtii Leonid  honorary member of ISSC science council

  • Yakushev Mikhail Vasilii  honorary member of ISSC science council

  • © 2004-2019 ИХТТ УрО РАН
    беременность, мода, красота, здоровье, диеты, женский журнал, здоровье детей, здоровье ребенка, красота и здоровье, жизнь и здоровье, секреты красоты, воспитание ребенка рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок медицина, клиники и больницы, болезни, врач, лечение, доктор, наркология, спид, вич, алкоголизм православные знакомства, православный сайт творчeства, православные рассказы, плохие мысли, православные психологи рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок