Structure, nonstoichiometry, sintering and oxygen permeability of perovskite SrCo1−2x(Fe,Nb)xO3−δ (x = 0.05, 0.10) oxides




  • a College of Chemistry and Materials Science, Liaoning University of Petroleum and Chemical Technology, Fushun 113001, PR China

  • b Greenhouse Gas Research Center, Climate Change Technology Research Division, Korea Institute of Energy Research, Daejeon 305-343, Republic of Korea

  • c State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, PR China



Corresponding author contact information

Corresponding author at: State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, PR China. Tel.: +86 411 8437 9180; fax: +86 411 8469 4447.


Corresponding author contact information

Corresponding author. Tel.: +82 42 860 3766; fax: +82 42 860 3134.









Abstract


The novel Fe/Nb co-substituted SrCo1−2x(Fe,Nb)xO3−δ (x = 0.05, 0.10) oxides have been synthesized and characterized by X-ray diffraction (XRD), differential scanning calorimetry (DSC), thermogravimetry (TG), and scanning electron microscopy (SEM). The XRD and DSC results demonstrate that the structural stability of the Fe/Nb co-substituted samples x = 0.05, 0.10 is improved greatly compared to the sample x = 0.00. The Fe/Nb co-doping in the SrCoO3−δ oxide results in the improved structural stability of the SrCo1−2x(Fe,Nb)xO3−δ (x = 0.05, 0.10) oxides. The nonstoichiometric and sintering properties were investigated by TG and SEM, and the oxygen permeation fluxes were measured at 800–950 °C for the sample x = 0.10. The improved oxygen permeability of the ceramic SrCo1−2x(Fe,Nb)xO3−δ (x = 0.10) membrane compared to the (Ba0.5Sr0.5)(Co0.8Fe0.2)O3−δ and SrCo0.8Fe0.2O3–δ membranes, was observed under an air/He oxygen partial pressure gradient at 800–950 °C.



Дизайн и программирование N-Studio 
А Б В Г Д Е Ё Ж З И Й К Л М Н О П Р С Т У Ф Х Ц Ч Ш Щ Ъ Ы Ь Э Ю Я
  • Chen Wev   honorary member of ISSC science council

  • Harton Vladislav Vadim  honorary member of ISSC science council

  • Lichtenstain Alexandr Iosif  honorary member of ISSC science council

  • Novikov Dimirtii Leonid  honorary member of ISSC science council

  • Yakushev Mikhail Vasilii  honorary member of ISSC science council

  • © 2004-2024 ИХТТ УрО РАН
    беременность, мода, красота, здоровье, диеты, женский журнал, здоровье детей, здоровье ребенка, красота и здоровье, жизнь и здоровье, секреты красоты, воспитание ребенка рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок медицина, клиники и больницы, болезни, врач, лечение, доктор, наркология, спид, вич, алкоголизм православные знакомства, православный сайт творчeства, православные рассказы, плохие мысли, православные психологи рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок